Nickel Copper Monel Plate
,Monel K500 Plate N05500
,Monel Uns N04400 Alloy
| Attribute | Value |
|---|---|
| Alloy | Nickel Copper Alloy |
| Density | 8.83g/cm³ |
| Surface | black or bright |
| Thickness | 3-50mm |
| Length | 6000mm |
| Width | 1500mm |
| Grade | Monel 400 UNS N04400 2.4360 NiCu30Fe |
| Grade | Monel K500 N05500 2.4375 |
| Type | Bar, plate, pipe, strip, etc |
| Surface treatment | Polishing, acid washing, electroplating, etc |
| Thermal stability | Excellent |
| Example | Nickel-based alloy materials with good corrosion resistance in sulfuric acid, hydrofluoric acid, hydrochloric acid, phosphoric acid, organic acids, alkaline media, salts and molten salts. |
Nickel copper alloy Monel 400 k500 N04400 N05500 Alloy plate Steel plate Petrochemical
Monel 400 alloy (UNS N04400 or MCu-28-1.5-1.8 or Ni68Cu28Fe) is a nickel-based alloy material with good corrosion resistance in seawater, chemical solvents, ammonia, sulfur, chlorine, hydrogen chloride, various acidic media such as sulfuric acid, hydrofluoric acid, hydrochloric acid, phosphoric acid, organic acids, alkaline media, salts and molten salts.
Monel 400 (Monel400, N04400) steel plate is a high-performance nickel-based alloy steel plate, which is widely used in various industrial fields due to its excellent corrosion resistance, high strength and good mechanical properties.
| Chinese name | Monel 400 alloy |
| Thermal conductivity | 21.8 W/m-K |
| Melting point | 1300 - 1350 °C |
| Magnetic properties | 200H (At 70 F) |
Monel 400 alloy has good mechanical properties, a wide range of operating temperatures from low to high temperatures, good welding performance and medium to high strength.
| Ni | Cu | Fe | Mn |
|---|---|---|---|
| about 63-70% | about 28-34% | about 2.5% | about 0.5% |
| Density | 0.318 lb / in3 8.80g/cm3 |
| Elastic modulus | 26 000 ksi |
| Heating energy | 0.427 J/g-°C |
| Temperature Range | Value |
|---|---|
| 70-200F | 7.7 |
| 70 - 400 F | 8.6 |
| 70 - 800 F | 8.9 |
| 70 - 1000 F | 9.1 |
| Shape | Tensile Strength | Yield Strength (0.2% Offset) | Elongation, % | Hardness |
|---|---|---|---|---|
| Rods | 70-110 ksi 480-760 MPa |
25-85 | 170-585 Brinell (3000-kg) 50-5 Rockwell B |
110min 60min |
| Plate | 70-95 ksi 482-655 MPa |
28-75 | 193-517 Brinell (3000-kg) 50-30 Rockwell B |
110-215 60-96 |
| Sheet | 70-120 ksi 482-827 MPa |
30-110 | 207-758 Brinell (3000-kg) 45-2 Rockwell B |
65min |
| Strip | 70-140 ksi 482-965 MPa |
25-130 | 172-896 Brinell (3000-kg) 50-2 Rockwell B |
68min |
| Seamless pipe | 70-130 ksi 482-896 MPa |
25-110 | 172-758 Brinell (3000-kg) 50-3 Rockwell B |
100max |
| Cold drawn wire | 70-180 ksi 482-1241 MPa |
30-170 | 207-1172 Brinell (3000-kg) 45-2 Rockwell B |
- |
Monel K500 alloy is a new type of alloy with excellent corrosion resistance and higher strength and hardness than Monel 400. This is because after adding Al, Ti and other elements to the alloy and undergoing certain heat treatment, dispersed intermetallic compounds exist on the matrix. The organizational structure is a single-phase austenite organization and is precipitated by dispersed Ni3 (Al, Ti) precipitates.
Monel K500 has about three times the yield strength and twice the tensile strength of Monel 400, and higher mechanical properties can be obtained through cold working or aging hardening. Monel K500 alloy has the same corrosion resistance as Monel 400 alloy.
Monel K500 alloy is mainly used for pump shafts and impellers, conveyor scrapers, oil well drill rings, elastic components, valve pads, etc. It can also be used to manufacture various heat exchange equipment, boiler feed water heaters, petroleum and chemical pipelines, containers, towers, tanks, valves, pumps, reactors, shafts, etc. Due to the low corrosion rate in flowing seawater and the high strength of this alloy, Monel K500 is suitable for manufacturing centrifugal pump shafts resistant to seawater corrosion. It is suitable for static and flowing seawater.
| Ni | Cu | Fe | Mn |
|---|---|---|---|
| 63% | 27-33% | 2% | 1.5% |